Application:

1. It is used as an important tempering part that requires good toughness, high strength, and large size, such as heavy machinery and high load shaft.

2. Turbine shaft with a diameter greater than 250 mm, rotor shaft of a helicopter.

3. Turbojet engine's turbine shaft, blades, high-load transmission parts, crankshaft fasteners, gears, etc.

4. It can also be used to operate rotor shafts and blades with temperatures exceeding 400 °C.

5. It can also be used to make important parts of special performance requirements after nitriding treatment. It can be used as ultra-high strength steel after low temperature tempering or after isothermal quenching.

1. Viene utilizzato come importante parte di tempra che richiede buona tenacità, alta resistenza e grandi dimensioni, come macchinari pesanti e albero di carico elevato.

2. Albero turbina con diametro maggiore di 250 mm, albero del rotore di un elicottero.

3. Albero della turbina del motore del turbogetto, pale, parti di trasmissione ad alto carico, dispositivi di fissaggio dell'albero motore, ingranaggi, ecc.

4. Può anche essere utilizzato per azionare alberi e pale del rotore con temperature superiori a 400 ° C.

5. Può anche essere utilizzato per realizzare parti importanti dei requisiti di prestazione speciali dopo il trattamento di nitrurazione. Può essere utilizzato come acciaio ad altissima resistenza dopo la tempera a bassa temperatura o dopo tempra isotermica.

JIMI STEEL.,LTD info@xingxionggroup.com for more information about the 4340 | 1.6511 | 40CrNi2MoA steel.

JIMI STEEL.,LTD info@xingxionggroup.comper ulteriori informazioni sull'acciaio 4340 | 1.6511 | 40CrNi2MoA.